(Click on grade number to download properties data sheet in PDF format.)
|
| Fusabond® Series/Grade |
MFR
(g/10 min) |
Melt Point (°C) |
MAH Graft Level |
Density (g/cc) |
Base Resin |
FDA Compliance |
Typical Use |
FUSABOND® P SERIES functionalized polypropylenes for coupling and adhesion |
Fusabond®
M-613-05 |
120 |
162 |
Medium |
-- |
Polypropylene Homopolymer |
21CFR 175.300 |
Coupling agent, short glass fiber filled PP and PP-WPC compounds |
Fusabond®
MD-353D |
23(a) (450) |
136 |
Very High |
-- |
Random Copolymer Polypropylene |
|
Coupling agent, long glass fiber filled PP compounds, and in PP pultrusion and glass mat processes; adhesion promoter |
FUSABOND® N SERIES nylon modifiers (See also A Series) |
Fusabond®
MF-416D |
23(b) |
29.8 |
High |
0.87 |
EPR |
21CFR 175.105 |
Premium PA 6,6 toughener |
Fusabond®
MN-493D |
1.6 |
48 |
Medium |
0.87 |
Ethylene-Octene Copolymer |
21CFR 175.105 |
Premium PA 6 toughener and general, all-purpose PA modifier |
Fusabond®
MO-525D |
3.7 |
51 |
High |
0.88 |
mPE |
|
Compatibilizer, PA-based polymer alloys, and general, all-purpose PA modifier |
FUSABOND® E SERIES functionalized ethylene-based modifiers for coupling and adhesion |
Fusabond®
EC-603D |
25 |
108 |
Very High |
|
Random Copolymer Polyethylene |
|
Compatibilizer for polyethylene-based recycle streams |
Fusabond®
MB-226DE
or
Fusabond®
MB-226DY |
1.5 |
122 |
High |
0.93 |
LLDPE |
21CFR 175.105 |
Compatibilizer; coupling agent for nonhalogen, flame-retarded Wire & Cable compounds containing fillers such as aluminum trihydrate (ATH) or magnesium hydroxide (Mg(OH)2) or for natural fiber (wood) plastic compounds |
Fusabond®
MB-265D |
12.3 |
131 |
High |
0.95 |
HDPE |
|
Compatibilizer; coupling agent for nonhalogen, flame-retarded Wire & Cable compounds containing fillers such as aluminum trihydrate (ATH) or magnesium hydroxide (Mg(OH)2) or for natural fiber (wood) plastic compounds |
Fusabond®
MB-439D |
2.7 |
115 |
High |
0.92 |
LLDPE |
|
Coupling agent for nonhalogen, flame-retarded Wire & Cable compounds containing fillers such as aluminum trihydrate (ATH) or magnesium hydroxide (Mg(OH)2) and/or calcium carbonate (CaCO3) |
Fusabond®
MB-528D |
6.8 |
114 |
Very High |
0.92 |
LLDPE |
|
Coupling agent for filled PE systems such as nonhalogen flame retardant filled Wire & Cable compounds; Adhesion promoter |
FUSABOND® C SERIES functionalized ethylene vinyl acetate (EVA) based modifiers for coupling and adhesion |
Fusabond®
MC-190D |
16.0 |
71 |
High |
0.95 |
EVA (28% VA) |
|
Adhesion promoter; coupling agent for nonhalogen, flame-retarded Wire & Cable compounds containing fillers such as aluminum trihydrate (ATH) or magnesium hydroxide (Mg(OH)2) |
Fusabond®
MC-250D |
1.5 |
71 |
Very High |
0.96 |
EVA (28%VA) |
|
Adhesion promoter; coupling agent for nonhalogen, flame-retarded Wire & Cable compounds containing fillers such as aluminum trihydrate (ATH) or magnesium hydroxide (Mg(OH)2) |
FUSABOND® A SERIES functionalized ethylene terpolymers for coupling and adhesion |
Fusabond®
EB-560D |
5.6 |
94 |
High |
-- |
EBA MAH Terpolymer |
|
Intermediate performance, all-purpose PA modifier; adhesion promoter and coupling agent, filled PA compounds |
Test Methods: MFR, ASTM D1238 (190°C, 2.16 kg) except as noted; melting point, ASTM D3418; density, ASTM D792
Note (a): MFR is measured at 160°C, 0.325 kg; value shown in (bracket) is calculated for 190°C, 2.16 kg
Note (b): MFR is measured at 280°C, 2.16 kg
Note (c): Liquid Displacement Method (DuPont)
|